Friction stir welding method and friction stir welded housing

ABSTRACT

A friction stir welding method utilizes a joining tool comprising a friction surface; a first workpiece comprising a first treating layer, a second workpiece comprising a second treating layer, and a joining member with a melting point lower than that of the first workpiece and the second workpiece. The joining member is arranged at the joining portion of the first workpiece and the second workpiece, and abutting the first workpiece and the second workpiece. The friction surface of the joining tool is positioned to resist at least one of the first treating layer and the second treating layer. The joining tool is rotated and moved to agitate at least one of the first workpiece and the second workpiece, until at least part of the first workpiece and the second workpiece are plasticized and joined together.

BACKGROUND

1. Technical Field

The present disclosure generally relates to friction stir welding, andparticularly, to a friction stir welding method using a joining toolwith no mixing pin and a friction stir welded housing.

2. Description of Related Art

Friction stir welding is widely used to join aluminum alloy because itis simple to execute.

The surface of the stir-welded housing can be uneven because thematerial of the stir-welded portion of the housing flows during frictionstir welding. After treatment, different aspects between the stir-weldedand non-stir-welded portions of the housing may be visible, creating anunfavorable appearance. Despite annealing, the difference of the joinedportion can persist.

Achievement of a favorable appearance in housings obtained by frictionstir welding remains a challenge.

Therefore, an improved friction stir welding method is desired toovercome the described limitations.

BRIEF DESCRIPTION OF THE DRAWINGS

The components in the drawings are not necessarily drawn to scale, theemphasis instead being placed upon clearly illustrating the principlesof the present disclosure. Moreover, in the drawings, like referencenumerals designate corresponding parts throughout several views.

FIG. 1 is a schematic view of a joining tool used in a first embodimentof a friction stir welding method of the disclosure.

FIG. 2 is a bottom view of the joining tool of FIG. 1.

FIG. 3 is a bottom view of a joining tool of a second embodiment of afriction stir welding method.

FIG. 4 is a schematic view of a first workpiece, a second workpiece anda joining member of the friction stir welding method of the disclosure.

FIG. 5 is a schematic view showing the joining tool friction stirringthe first workpiece and the second workpiece of FIG. 4.

FIG. 6 is a schematic view of a welded housing joined by the frictionstir welded method of the disclosure.

FIG. 7 is a flowchart of a friction stir welding method as disclosed.

DETAILED DESCRIPTION

Referring to FIGS. 1 and 4, a joining tool 10 is used to join a firstworkpiece 60 and a second workpiece 70 in a friction stir welding methodas disclosed. The joining tool 10 is substantially cylindrical andincludes a friction surface 11. The friction surface 11 is substantiallyflat. The joining tool 10 defines a slot in the friction surface 11. Theslot may be spiral slot 13 a as shown in FIG. 2, and may include aplurality of curved slots 13 b originating at a rotation axis of thejoining tool 10, as shown in FIG. 3.

Referring to FIGS. 1, 4 and 5, the first workpiece 60 includes a firsttreating layer 61 and a first joining surface 63 angled therewith. Thefirst workpiece 60 further defines a first groove 67 from the firstjoining surface 63, at an end of the first workpiece 60 away from thefirst treating layer 61. The second workpiece 70 includes a secondtreating layer 71 and a second joining surface 73 angled therewith. Thesecond workpiece 70 further defines a second groove 77 from the secondjoining surface 73. When the first workpiece 60 and the second workpiece70 are arranged together, the first groove 67 and the second groove 77cooperatively form a receiving slot (not labeled).

Before joining the first workpiece 60 and the second workpiece 70, ajoining member 400 with a melting point lower than that of the firstworkpiece 60 and the second workpiece 70 is arranged in the receivingslot between the first workpiece 60 and the second workpiece 70. Thefirst workpiece 60 and the second workpiece 70 are fixed abutting eachother, wherein the first joining surface 63 contacts the second joiningsurface 73. An angle is defined by the first treating layer 61 of thefirst workpiece 60 and the second treating layer 71 of the secondworkpiece 70. The angle may be any degree other than 0° or 180°. In theillustrated embodiment, the angle is about 90°. The first joiningsurface 63 and the second joining surface 73 define a joint line (notlabeled) therebetween, at an edge of the corner defined by the firstworkpiece 60 and the second workpiece 70.

Referring to FIGS. 1, and 4 through 7, the method of the friction stirwelding method is described as follow. In step S701, a joining tool 10comprising a friction surface 11 is provided. In step S702, a firstworkpiece 60 comprising a first treating layer 61 is provided. In stepS703, a second workpiece 70 comprising a second treating layer 71 isprovided. In step S704, a joining member 400 is provided, the joiningmember 400 has a melting point lower than that of the first workpiece 60and the second workpiece 70. In step S705, the joining member 400 isarranged at a joining portion of the first workpiece 60 and the secondworkpiece 70, and the first workpiece 60 abuts the second workpiece 70.In step S706, the friction surface 11 of the joining tool 10 resists thefirst treating layer 61 of the first workpiece 60. In step S707, joiningtool 10 rotates along the axis thereof relative to the first workpiece60 and the second workpiece 70 and moves along the joint line. Thus, thejoining tool 10 produces a local region of highly plasticized materialsuch that the first workpiece 60 and the second workpiece 70 diffuseamong each other. As such, the first workpiece 60 and the secondworkpiece 70 are joined to form a friction stir welded housing 300.

When heat created by the friction stir-welded first workpiece 60 istransmitted to the first groove 67 and the second groove 77, thematerial of the joining member 400, with a lower melting point,plasticizes before the first workpiece 60 and the second workpiece 70.Heat transmitted adjacent to the receiving slot need not raise thetemperature adjacent thereto to that of the first workpiece 60 and thesecond workpiece 70, while raising the temperature to the melting pointof the joining member 400. Thus, material of the joining member 400flows in the receiving slot to join with and enhance the joiningstrength of the first workpiece 60 and the second workpiece 70.

Alternatively, the receiving slot may be only defined in the firstworkpiece 60 or the second workpiece 70. A joining member 400 may bepositioned inbetween the first workpiece 60 and the second workpiece 70.The joining member 400 may be solder.

In the disclosed friction stir welding methods, only the joiningportions of the workpieces need be machined, such that the joining tool10 is small, with a correspondingly low driving force thereof required.Thus, equipment applying the joining tool 10 to friction stir welding issimple and low cost.

In the embodiment, after the first workpiece 60 is joined to the secondworkpiece 70, surface layers adjacent to the first treating layers 61and the second treating layer 71 may be removed. That is, material witha changed metal structure is removed and material with unchanged metalstructure is exposed. Therefore, the housing 300 formed by the abovedescribed friction stir welding method can provide a favorableappearance, even after subsequent treatment such as an anodic process.

In the joining method disclosed, a rotation direction of the joiningtool 10 is the same as the extending direction from a center to aperiphery of the joining tool 10. The joining tool 10 rotates at a highspeed and moves at a low speed, and an end of the joining tool 10extends slightly into the first workpiece 60 and the second workpiece70. A rotation speed S, operating velocity V, and stir-welded depth H ofthe first workpiece 60 and the second workpiece 70 are determined byvarious factors, such as the material and thickness of the firstworkpiece 60 and the second workpiece 70, and the size and material ofthe joining tool 10, so long as the first workpiece 60 and the secondworkpiece 70 can be joined. In the illustrated embodiment, the firstworkpiece 60 and the second workpiece 70 are aluminum alloy plates, therotation speed S is about 7000 rpm, the operating velocity V is about500 mm/min, and the stir-welding depth H is about 0.15 mm.

The first workpiece 60 and the second workpiece 70 may be a materialwith low melting point, such as aluminum, aluminum alloy, copper alloy,or rubber, and be of any shape. A material of the joining tool 10 is acritical factor in selecting the material of the first workpiece 60 andthe second workpiece 70. The increased melting point of the joining tool10 allows a higher melting point of the material of the first workpiece60 and the second workpiece 70. The melting point of the joining tool 10must exceed those of the first workpiece 60 and the second workpiece 70.Joining portions of the workpieces may be a point, line or surface.

In the disclosed friction stir welding methods, only the joint of theworkpieces need be machined, such that the joining tool 10 is small,with a correspondingly low driving force thereof required. Equipmentapplying the joining tool 10 to friction stir weld is simple and lowcost.

The joining tool 10 may be applied in ordinary machining centers,whereby workpieces may be machined and joined at the same machiningcenter. As such, the workpieces need only be clamped once, thusimproving machining efficiency and precision. In addition, no specialmachinery is needed. Furthermore, the friction stir welding method canbe used to join workpieces with complex joining surfaces together.

Finally, while various embodiments have been described and illustrated,the disclosure is not to be construed as being limited thereto. Variousmodifications can be made to the embodiments by those skilled in the artwithout departing from the true spirit and scope of the disclosure asdefined by the appended claims.

1. A friction stir welding method, comprising: providing a joining toolcomprising a friction surface; providing a first workpiece comprising afirst treating layer, and a first joining surface slanted to the firsttreating layer; providing a second workpiece angled to the firstworkpiece, the second workpiece comprising a second treating layer, anda second joining surface slanted to the second treating layer; providinga joining member with a melting point lower than that of the firstworkpiece and the second workpiece; arranging the joining member at ajoining portion of the first joining surface of the first workpiece andthe second joining surface of the second workpiece, and abutting thefirst joining surface of the first workpiece and the second joiningsurface of the second workpiece; positioning the friction surface of thejoining tool to resist at least one of the first treating layer and thesecond treating layer; and rotating and moving the joining tool toagitate at least one of the first workpiece and the second workpiece,until at least part of the first workpiece and the second workpiece areplasticized and joined together.
 2. The friction stir welding method ofclaim 1, wherein the friction surface of the joining tool resists thefirst treating layer of the first workpiece.
 3. The friction stirwelding method of claim 2, wherein the first workpiece is perpendicularto the second workpiece, and the friction surface of the joining toolresists the first treating layer of the first workpiece.
 4. (canceled)5. The friction stir welding method of claim 1, wherein the firstworkpiece further defines a first groove from the first joining surface,in which the joining member is received.
 6. The friction stir weldingmethod of claim 5, wherein the second workpiece further defines a secondgroove from the second joining surface; the first groove of the firstworkpiece and the second groove of the second workpiece cooperativelydefine a receiving slot receiving the joining member. 7-9. (canceled)10. The friction stir welding method of claim 1, wherein the joiningmember is solder.
 11. The friction stir welding method of claim 1,further comprising a step of removing a surface layer of the stir-weldedfirst workpiece or second workpiece, after joining the first workpieceand the second workpiece.
 12. The friction stir welding method of claim11, wherein the removed material is material which has changed instructure from agitation.
 13. The friction stir welding method of claim11, wherein surface layers of both the first workpiece and the secondworkpiece are removed.
 14. The friction stir welding method of claim 1,wherein the friction surface of the joining tool is substantially flat,and the joining tool defines a slot in the friction surface.
 15. Thefriction stir welding method of claim 14, wherein the slot is spiral.16. The friction stir welding method of claim 14, wherein the slot iscurved slots originating at a rotation axis of the joining tool. 17-18.(canceled)